Title: Electrodeposition of Ni-Mo-rGO composite electrodes for efficient hydrogen production in an alkaline medium
Authors: Shetty, S.
Sadiq, M.M.J.
Bhat, D.K.
Hegde, A.C.
Issue Date: 2018
Citation: New Journal of Chemistry, 2018, Vol.42, 6, pp.4661-4669
Abstract: The mechanism and kinetics of the hydrogen evolution reaction (HER) on Ni-Mo-rGO composite electrodes in 1.0 M KOH solution were investigated by cyclic voltammetry (CV), chronopotentiometry (CP) and potentiodynamic polarization techniques. Ni-Mo-rGO composite coatings were deposited on a copper substrate by an electrodeposition method at a current density (c.d.) ranging from 1.0 to 4.0 A dm-2. The change in surface morphology and chemical composition was characterized by scanning electron microscopy (SEM), X-ray diffraction (XRD) analysis, energy dispersive X-ray (EDX) analysis and X-ray photoelectron spectroscopy (XPS). It was shown that the carbon content of the composite coatings was affected by c.d. With the increase in the carbon content in the Ni-Mo-rGO composite coatings, the onset potential was decreased and the exchange current density was increased during the HER. The minimum onset potential and maximum exchange current density of Ni-Mo-rGO composite coatings for the HER were -401.6 mV and 4.31 ?A cm-2. The best composite coating exhibited a maximum peak current density of -0.517 A cm-2 at -1.6 V, which is approximately 3 times better than that of the binary Ni-Mo alloy, indicating the best activity for hydrogen production. The potentiodynamic polarization measurements revealed that composite coatings are much more resistant to corrosion than binary alloy coatings. 2018 The Royal Society of Chemistry and the Centre National de la Recherche Scientifique.
URI: http://idr.nitk.ac.in/jspui/handle/123456789/11101
Appears in Collections:1. Journal Articles

Files in This Item:
File Description SizeFormat 
40.Electrodeposition of Ni–Mo–rGO.pdf3.21 MBAdobe PDFThumbnail
View/Open


Items in DSpace are protected by copyright, with all rights reserved, unless otherwise indicated.